镍基钎料

The nickel-based brazing alloy BrazeLet BNi1 provides high strength joints with excellent oxidation resistance suitable for brazing stainless steels and nickel-based superalloys. It is suitable for brazing in vacuum or protective atmospheres (dry hydrogen or argon). Joint properties can be further improved by employing a diffusion hold after brazing. The brazing alloy is typically used for joining parts subjected to high stresses and temperatures such as turbine components.

The nickel-based brazing alloy BrazeLet BNi1A provides high strength joints with excellent oxidation resistance suitable for brazing stainless steels and nickel-based superalloys. It is suitable for brazing in vacuum or protective atmospheres (dry hydrogen or argon). The alloy is similar to BrazeLet BNi1, but has low carbon content. Joint properties can be further improved by employing a diffusion hold after brazing. The brazing alloy is typically used for joining parts subjected to high stresses and temperatures such as turbine components and diamond tools.

镍基钎焊合金BrazeLet^® BNi2在真空或保护气氛中对不锈钢材料进行钎焊时提供高强度。 钎焊合金通常用于热交换器钎焊，如汽车EGR冷却器或者家用或工业自来水应用，这些应用不需要高耐腐蚀性。

BrazeLet BNi2中含有硼作为降熔元素，因此可在较低的温度下使用。

成分

ISO 3677、B-Ni82CrSiBFe-970/1000
ISO 17672、Ni 620
ANSI/AWS A5.8、BNi-2
UNS N99620

熔化温度范围

970-1000°C

最低钎焊温度

1050°C

The nickel-based brazing alloy BrazeLet BNi2 provides high strength when brazing stainless steel material in vacuum or protective atmospheres (hydrogen or argon). It provides excellent high temperature strength and oxidation resistance. Joint properties can be further improved by employing a diffusion hold after brazing. It is a versatile brazing filler metal used in aerospace, automotive and industrial applications such as heat exchangers and turbines.

The brazing paste BrazeLet Ni2DW-9201 can be used for dispensing applications, typically found on heat exchanger inlet and outlet tubes, housing to core joints and hole plate to tube joints. It can be dispensed by using standard air pressure dispensing units. For better precision, screw dispense units are recommended. The paste sticks on all bevel positions without the need of pre-drying but is easily removed using water. The paste formulation offers the highest metal content of our standard dispensing pastes.

BrazeLet Ni2DW-9201 properties allow reliable application in a wide speed range as a result of the dispensing equipment / automatisation as well as the needle diameter. The paste can be delivered in cartridges for use in automated applications or different sized cans for refilling of smaller cartridges for manual applications. For best performance, it is recommended to first stir the paste.

The nickel-based brazing alloy BrazeLet BNi3 provides high strength joints when brazing in vacuum or protective atmospheres (hydrogen or argon). As it is Cr-free it is less sensitive to marginal furnace atmospheres. The brazing alloy is typically used for brazing nickel-based superalloys and stainless steel components where high elevated temperature strength is important, such as turbine vanes or honeycomb seals. The alloy also has good oxidation resistance. Joint properties can be further improved by employing a diffusion hold after brazing.

The nickel-based brazing alloy BrazeLet BNi4 provides high strength joints when brazing in vacuum or protective atmospheres (hydrogen or argon). As it is Cr-free it is less sensitive to marginal furnace atmospheres. The brazing alloy is typically used for brazing nickel-based superalloys and stainless steel components where high elevated temperature strength is important, such as turbine vanes and honeycomb seals. The alloy also has good oxidation resistance. Joint properties can be further improved by employing a diffusion hold after brazing. Compared to the similar BrazeLet BNi3, BrazeLet BNi4 has better gap filling ability and provides more ductile joints.

BrazeLet^® BNi5是一种镍基钎焊合金，在真空或保护气氛钎焊中对不锈钢材料具有良好的润湿性。 

高含量的合金铬具有良好的耐高温气体和酸腐蚀性能。 BrazeLet BNi5的熔化温度范围很高，因此适合用于极高温度下的应用，例如用于汽车和卡车金属催化转化器的EGR冷却器。

成分

ISO 3677、B-Ni71CrSi-1080/1135
ISO 17672、Ni 650
ANSI/AWS A5.8、BNi-5
UNS N99650

熔化温度范围

1080-1135°C

最低钎焊温度

1150°C

The nickel-based brazing alloy BrazeLet BNi5 has good wetting behaviour on stainless steels and nickel-based superalloys and is suitable for brazing in vacuum or protective atmospheres (hydrogen or argon). The high level of alloyed chromium results in a good hot gas and acid corrosion resistance. The high melting range of BrazeLet BNi5 makes it suitable for applications working at very high temperatures, for instance EGR coolers for trucks, automotive metal catalytic converters and turbine vanes. It is also a commonly used filler material for industrial heat exchangers. Joint properties can be further improved by employing a diffusion hold after brazing.

The brazing paste BrazeLet Ni5DW-9201 can be used for dispensing applications, typically found on heat exchanger inlet and outlet tubes, housing to core joints and hole plate to tube joints. It can be dispensed by using standard air pressure dispensing units. For better precision, screw dispense units are recommended. The paste sticks on all bevel positions without the need of pre-drying but is easily removed using water. The paste formulation offers the highest metal content of our standard dispensing pastes.

BrazeLet Ni5DW-9201 properties allow reliable application in a wide speed range as a result of the dispensing equipment / automatisation as well as the needle diameter. The paste can be delivered in cartridges for use in automated applications or different sized cans for refilling of smaller cartridges for manual applications. For best performance, it is recommended to first stir the paste.

The nickel-based brazing alloy BrazeLet BNi6 is a free-flowing material suitable for brazing low-carbon steels and stainless steels. It is suitable for brazing in vacuum or protective atmospheres (dry hydrogen, nitrogen/hydrogen mixtures or argon) and is also suitable for marginal furnace atmospheres. It allows brazing at lower temperatures than any of the other nickel-based brazing alloys. It is particularly suitable for brazing deep narrow joints as it maintains the excellent flowability with limited P diffusion into most base materials. It is recommended that gaps do not exceed 30 µm as wider gaps risk the formation of a crack-sensitive brittle centre line.

BrazeLet^® BNi7是一种在真空或保护气氛中对不锈钢材料进行钎焊时提供高强度的镍基钎焊合金。 这种钎焊合金的典型应用是不需要高耐腐蚀性的热交换器，例如汽车EGR冷却器和家用或工业自来水应用。

BrazeLet BNi7中含有磷作为降熔元素，因此可在较低的温度下使用。

成分

ISO 3677、B-Ni76CrP-890
ISO 17672、Ni 710
ANSI/AWS A5.8、BNi-7
UNS N99710

熔化温度

890°C

最低钎焊温度

980°C

The nickel-based brazing alloy BrazeLet BNi7 is a free-flowing material suitable for brazing stainless steels. It is suitable for brazing in vacuum or protective atmospheres (dry hydrogen or argon). It allows brazing at lower temperatures than most of the other nickel-based brazing alloys. It is particularly suitable for brazing deep narrow joints as it maintains the excellent flowability with limited P diffusion into most base materials. It is recommended that gaps do not exceed 30 µm as wider gaps risk the formation of a crack-sensitive brittle centre line. Typical applications for this brazing alloy include thin-walled components such as honeycomb seals, industrial heat exchangers and tubular heating elements for drinking water applications.

The brazing paste BrazeLet Ni7DW-9201 can be used for dispensing applications, typically found on heat exchanger inlet and outlet tubes, housing to core joints and hole plate to tube joints. It can be dispensed by using standard air pressure dispensing units. For better precision, screw dispense units are recommended. The paste sticks on all bevel positions without the need of pre-drying but is easily removed using water. The paste formulation offers the highest metal content of our standard dispensing pastes.

BrazeLet Ni7DW-9201 properties allow reliable application in a wide speed range as a result of the dispensing equipment / automatization as well as the needle diameter. The paste can be delivered in cartridges for use in automated applications or different sized cans for refilling of smaller cartridges for manual applications. For best performance, it is recommended to first stir the paste.

The nickel-based brazing alloy BrazeLet Ni613, features a best in class wetting behaviour on stainless steel material in vacuum or protective atmosphere (dry hydrogen or argon). Its high level of alloyed chromium results in a superior hot gas and acid corrosion resistance. The brazing alloy is best suited for brazing heat exchangers such as exhaust gas recirculation (EGR) coolers in automotive or drinking water applications. Compared to most of the standard nickel-based brazing alloys, BrazeLet Ni613 is able to fill larger gaps without brittle phase lines or cracks. The resulting micro hardness in the brazed joint microstructure is less than half when compared to BrazeLet BNi5. This leads to a more reliable and safe brazing as well as more flexibility in part tolerances.

The brazing paste BrazeLet Ni613D-9004 can be used for dispensing applications, typically found on heat exchanger inlet and outlet tubes, housing to core joints and hole plate to tube joints. It can be dispensed by using standard air pressure dispensing units. For better precision, screw dispense units are recommended. The paste sticks on all bevel and vertical positions without the need of pre-drying but is easily removed using aliphatic solvents.

BrazeLet Ni613D-9004 properties allow reliable application in a wide speed range as a result of the dispensing equipment / automatisation as well as the needle diameter. The paste can be delivered in cartridges for use in automated applications or different sized cans for refilling of smaller cartridges for manual applications. It has no settlements. However, when opening a can from stock it is always recommended to stir the paste.

The nickel-based brazing alloy BrazeLet Ni613, features a best in class wetting behaviour on stainless steel material in vacuum or protective atmosphere (dry hydrogen or argon). Its high level of alloyed chromium results in a superior hot gas and acid corrosion resistance. The brazing alloy is best suited for brazing heat exchangers such as exhaust gas recirculation (EGR) coolers in automotive or drinking water applications. Compared to most of the standard nickel-based brazing alloys, BrazeLet Ni613 is able to fill larger gaps without brittle phase lines or cracks. The resulting micro hardness in the brazed joint microstructure is less than half when compared to BrazeLet BNi5. This leads to a more reliable and safe brazing as well as more flexibility in part tolerances.

The water-based brazing paste BrazeLet Ni613DW-9003 can be used for dispensing applications, typically found on heat exchanger inlet and outlet tubes, housing to core joints and hole plate to tube joints. It can be dispensed by using standard air pressure dispensing units. For better precision, screw dispense units are recommended. The paste sticks on all bevel and vertical positions without the need of pre-drying but is easily removed using water.

BrazeLet Ni613DW-9003 properties allow reliable application in a wide speed range as a result of the dispensing equipment / automatisation as well as the needle diameter. The paste can be delivered in cartridges for use in automated applications or different sized cans for refilling of smaller cartridges for manual applications. For best performance, it is recommended to first stir it.

The nickel-based brazing alloy BrazeLet Ni613, features a best in class wetting behaviour on stainless steel material in vacuum or protective atmosphere (dry hydrogen or argon). Its high level of alloyed chromium results in a superior hot gas and acid corrosion resistance. The brazing alloy is best suited for brazing heat exchangers such as exhaust gas recirculation (EGR) coolers in automotive or drinking water applications. Compared to most of the standard nickel-based brazing alloys, BrazeLet Ni613 is able to fill larger gaps without brittle phase lines or cracks. The resulting micro hardness in the brazed joint microstructure is less than half when compared to BrazeLet BNi5. This leads to a more reliable and safe brazing as well as more flexibility in part tolerances.

The brazing paste BrazeLet Ni613DW-9201 can be used for dispensing applications, typically found on heat exchanger inlet and outlet tubes, housing to core joints and hole plate to tube joints. It can be dispensed by using standard air pressure dispensing units. For better precision, screw dispense units are recommended. The paste sticks on all bevel positions without the need of pre-drying but is easily removed using water. The paste formulation offers the highest metal content of our standard dispensing pastes.

BrazeLet Ni613DW-9201 properties allow reliable application in a wide speed range as a result of the dispensing equipment / automatisation as well as the needle diameter. The paste can be delivered in cartridges for use in automated applications or different sized cans for refilling of smaller cartridges for manual applications. For best performance, it is recommended to first stir the paste.

The nickel-based brazing alloy BrazeLet Ni613, features a best in class wetting behaviour on stainless steel material in vacuum or protective atmosphere (dry hydrogen or argon). Its high level of alloyed chromium results in a superior hot gas and acid corrosion resistance. The brazing alloy is best suited for brazing heat exchangers such as exhaust gas recirculation (EGR) coolers in automotive or drinking water applications. Compared to most of the standard nickel-based brazing alloys, BrazeLet Ni613 is able to fill larger gaps without brittle phase lines or cracks. The resulting micro hardness in the brazed joint microstructure is less than half when compared to BrazeLet BNi5. This leads to a more reliable and safe brazing as well as more flexibility in part tolerances.

The brazing paste BrazeLet Ni613P-9012 is typically in use for printing thick paste layers of about 0.2 to 0.6 mm on flat parts or on top of structured parts by use of screens or stencils. A typical application is printing of paste on hole plates of tube bundled heat exchangers. The use of rubber squeegees is recommended. Reliable printing requires precise positioning fixture tool by use of vacuum table or clamping device. Typical printing speed is 100 mm/s. Thin printing lines should at least have a width twice the printing thickness and the small dots diameter should be three times the printing thickness or greater. Printing accuracy is very precise as the paste maintains its shape during drying.
 
The solvent based BrazeLet Ni613P-9012 increases productivity wherever drying of the paste is an issue. It has no settlement, and no stirring is needed in the equipment. However, when opening a can from stock it is always recommended to stir the paste. The printed parts can be dried with standard drying process (hot air) at 120 – 170 °C. Here, the drying time needs to be established as it varies depending on thermal mass, parts design and the used furnace. After drying, the paste has excellent adhesion to the metal sheet.

The nickel-based brazing alloy BrazeLet Ni613, features a best in class wetting behaviour on stainless steel material in vacuum or protective atmosphere (dry hydrogen or argon). Its high level of alloyed chromium results in a superior hot gas and acid corrosion resistance. The brazing alloy is best suited for brazing heat exchangers such as exhaust gas recirculation (EGR) coolers in automotive or drinking water applications. Compared to most of the standard nickel-based brazing alloys, BrazeLet Ni613 is able to fill larger gaps without brittle phase lines or cracks. The resulting micro hardness in the brazed joint microstructure is less than half when compared to BrazeLet BNi5. This leads to a more reliable and safe brazing as well as more flexibility in part tolerances.

The brazing paste BrazeLet Ni613R-9003 can be used for roller coating fins or structured plates, typically found in flat heat exchanger designs. Depending on type of roller used the paste can be applied with thin layers either on top or on the side of the fin tips. Gap size between the paste roll and the scraper of 0.08 – 0.12 mm is recommended. The amount of paste is controlled by weight and is a function of the fins or structured plate design. BrazeLet Ni613R-9003 properties allow reliable application in a wide range of coating speeds, tested with good results from 3 m/min up to 20 m/min. The oil-based paste ensures reliable coating over time without drying on the roll. BrazeLet Ni613R-9003 has higher metal content and lower binder content compared to standard roller coating pastes, which decreases packaging and transportation needs for the same amount of brazing filler metal.

The coated fins can be dried with standard drying process (hot air) at 120 – 170 °C. The drying time depends on thermal mass, parts design and the used furnace and thus needs to be established. When dried, the paste has excellent adhesion to the metal sheet.

Höganäs’ unique and patented nickel-based brazing alloy BrazeLet Ni623 is a high temperature brazing alloy suitable to use where both base material and the brazed joints require superior corrosion resistance. The alloy is developed and particularly suitable for brazing high-alloyed austenitic and super-austenitic stainless steels which require special heat treatments and rapid cooling from temperatures around 1100 °C to avoid precipitation of deleterious intermetallic phases.